粉末硬度化学成分（重量%）典型用途CCrSiWFeMoNiCoMnBStellite 1482.4030.501.0012.503.001.003.00Bal0.25阀座、轴承、刀口等Stellite 3482.3030.501.0012.503.002.50Bal针阀座、阀座、轧钢导向辊Stellite 6381.1529.001.104.003.001.003.00Bal0.50发动机气门、高温高压阀门、涡轮机叶片Stellite 12421.4029.501.458.253.001.003.00Bal1.00高温高压阀门、锯齿、螺旋推杆等Stellite 20522.4532.501.0017.53.001.003.00Bal0.50轴承套筒、耐磨板Stellite 21280.2527.502.000.152.005.502.50Bal1.00涡轮机叶片、各种流体阀、阀座等Stellite 25冷硬0.1020.001.0015.003.001.0010.00Bal1.50冲压、挤压模具Stellite 31310.5025.501.007.502.0010.50Bal1.00挤压模、燃气涡轮叶片Stellite 156431.6028.001.154.500.501.003.00Bal1.00高温高压阀门、热锻模Stellite 157500.1022.001.604.503.000.303.00Bal0.302.40摩托车阀顶端Stellite 158400.7526.001.905.503.000.503.00Bal0.100.70高温高压阀门、锯齿、螺旋推杆等Stellite 158W411.3031.001.505.504.502.00Bal0.70阀座、高温高压阀门等Stellite F371.7525.501.1012.003.000.6022.50Bal0.50内燃机进排气阀Tribaloy X-400.8525.000.307.501.0010.00Bal0.30冲压、挤压模具燃气涡轮叶片Tribaloy 400530.088.502.601.5028.501.50Bal用于高温强腐蚀介质中的闸阀、挤塑器Tribaloy 800530.0818.003.401.5028.501.50Bal用于高温强腐蚀介质中的闸阀、挤塑器Tribaloy 9000.0818.002.70Mo:232.5016.00Bal阀座、密封圈、高温热轧辊stellite SF6410.7019.002.307.503.0013.50Bal1.001.70发动机气门、高温高压阀门Stellite SF12431.0019.002.809.003.0013.00Bal1.001.80高温高压阀门、热剪切刀刃等Stellite 706401.1029.002.00Mo:52.002.00Bal发动机气门、高温高压阀门Stellite 712471.9029.002.00Mo:8.52.002.00Bal高温高压阀门、螺旋推杆粉末硬度化学成分（重量%）典型用途Haystellite 16050%Deloro60+50%WC（铸造cast）混料机叶片、刮板、风机叶片Haystellite 26065%Deloro60+35%WC（铸造cast）混料机叶片、刮板、风机叶片Haystellite 36085%Deloro60+15%WC（铸造cast）混料机叶片、刮板、风机叶片Haystellite 46040%Deloro60+60%WC（铸造cast）混料机叶片、刮板、风机叶片Haystellite 76070%Deloro60+30%WC（铸造cast）混料机叶片、刮板、风机叶片Haystellite 86060%Deloro60+40%WC（铸造cast）混料机叶片、刮板、风机叶片NiWC 256075%Ni60+25%WC混料机叶片、刮板、风机叶片NiWC 356065%Ni60+35%WC风机叶片、螺旋输入器等JK112110(HV)12%Co/88%WC球阀、压缩机轴、泵密封圈等JK1171010(HV)17%Co/83%WC阀门、导向杆、压纸辊等JK1201000(HV)10%Co/4%Cr/86%WC球阀、吸纸辊等JK135850(HV)25%（80%Ni/20%Cr）/75%Cr3C2密封环  ，阀门、汽轮机叶片JK576550(HV)同Stellite6高温高压阀门JK6153800(HV)50%WC+50%Deloro 60拉丝塔轮、泵部件粉末硬度化学成分（重量%）典型用途CCrSiWFeMoNiCoMnBNi 25250.203.508.00Bal1.50玻璃模具、各类成型模Ni 35350.3010.503.5010.00Bal2.00玻璃模具、各类成型模Ni 45450.4512.004.0010.00Bal0.102.40排气阀密封面、柱塞Ni 55550.7515.504.0014.003.00Bal3.00模具、凸轮、柱塞及排阀Ni 60590.8015.504.003.0015.00Bal3.50柱塞、拉丝辊筒、凸轮、机械易损件Ni 62611.0015.503.8014.00BalW:10.54.00造纸机磨盘、铲车铲齿Nistelle B冷硬0.101.001.00V:0.35.0028.00Bal2.50高温耐蚀密封环Deloro 20200.034.502.00Bal0.70玻璃模具、各类成型模等Deloro 22<, SPAN style="FONT, -SIZE: 9pt; FONT-FAMILY: 宋体; COLOR: black; mso-font-kerning: 0pt; mso-bidi-font-family: 宋体">220.200.102.850.50Bal0.501.45玻璃模具、各类成型模Deloro 22M2220.053.002.30Bal0.80玻璃模具、各类成型模等Deloro 28280.050.102.80Bal1.00玻璃模具、各类成型模等Deloro 30300.152.502.601.00Bal0.301.40滑轮、齿轮齿Deloro 35350.204.003.201.400.10Bal0.101.60玻璃模具、阀座Deloro 37360.154.502.60Bal1.00玻璃模具、各类成型模等Deloro 40400.307.503.502.300.10Bal0.101.70螺旋送料器、模芯等,Deloro 50500.4011.004.002.700.10Bal0.102.20泵轴、纸浆刀、阀门、密封环、轴套Deloro60590.6515.004.304.000.10Bal0.103.10挤压模、螺旋筒体、泵叶、柱塞Deloro6325570.5016.004.003.004.503.00Bal0.103.50耐蚀泵轴、轴套Tribaloy 700540.0815.53.401.5032.50Bal1.50核工业应用抗蚀抗氧化抗辐射粉末硬度化学成分（重量%）典型用途CCrSiWFeMoNiCoMnBHK1582.51025Bal102.5离心浇注用粉HK3581104463Bal103.5离心浇注用粉HK5638.5522.5Bal112.5离心浇注用粉HK761222.55.5Bal3离心浇注用粉NiCo5621194646Bal102.5离心浇注用粉NiCo10560.583.54Bal

焊条牌号型号主要用途硬度HS101～用于堆焊要求耐磨损、抗氧化或耐气蚀的场合  ，如铲斗齿、泵套、柴油机的汽门、排气叶片等 。 HRC≥48-54HS111RCoCr-A用于要求在高温工作时能保持良好的耐磨性及耐蚀性  ，如高温、高压阀门、热剪切刀刃、热锻模等HRC≥40-45HS112RCoCr-B用于高温、高压阀门、内燃机阀、高压泵轴套和内衬套筒、热轧辊孔型等堆焊HRC≥40-45HS113～用于牙轮钻头轴承、锅炉的旋转叶片、粉碎机刃口、螺旋送料机等堆焊HRC≥55-60HS113G～用于泵的套筒和旋转密封环、磨损面板、轴承套筒、高温热轧辊、油田钻头等堆焊HRC≥54HS113Ni～用于耐气蚀、耐腐蚀性能要求较高的内燃机气门、排气阀的堆焊HRC≥37-40   HS114RCoCr-C用于耐气蚀、耐腐蚀性能要求较高的内燃机气门、排气阀的堆焊HRC≥52HS115RCoCr-E该焊丝是用钼强化的低碳钴铬合金  ，在室温下硬度较低  ，但冷作后硬度有所提高 。 堆焊层具有良好的耐高温腐蚀  ，耐冲击能和良好的高温强度HRC≥27HS116RCoCr-C有较高的耐磨损性和高温强度  ，但韧性较差  ，在耐硫酸、磷酸、硝酸等工况条件下呈优良的耐腐蚀性 。 主要用于铜基及铝基合金的热压模等堆焊HRC≥46-50HS117～有较强的耐磨料磨损及耐腐蚀性能  ，在800℃高温也能保持这些特性 。 用于泵的套筒和旋转密封环等磨损面的堆焊HRC≥53

D802钴基堆焊焊条  型号：EDCoCr-A-03  说明：钴铬钨合金焊芯的钴基堆焊焊条  ，采用直流反接  ，堆焊金属在650℃工作仍能保持良好的耐磨性和耐腐蚀性 。   用途：用于在650℃左右工作仍能保持良好的耐磨性和耐腐蚀性的场合  ，或承受冲击和冷热交错的部位  ，如堆焊高温高压阀门及热剪刀刃等 。   熔敷金属化学成分/%  C 0.7-1.44 Si≤2  Mn≤2 Cr 25-32 Fe≤4 W 3-6 其他≤4 余量为Co堆焊硬度HRC：≥40  D812钴基堆焊焊条  型号：EDCoCr-B-03  说明：钴铬钨合金焊芯的钴基堆焊焊条  ，采用直流反接  ，堆焊金属在650℃工作仍能保持良好的耐磨性和耐腐蚀性 。   用途：用于高温高压阀门、高压泵的轴套筒和内衬套以及化纤设备的斩刀刃口等 。 熔敷金属化学成分/%  C 1-1.7 Si≤2  Mn≤2 Cr 25-32  Fe≤5 W 7-10 其他≤4 余量为Co  堆焊硬度HRC：≥44  D822钴基堆焊焊条  型号：EDCoCr-C-03  说明：高碳钴铬钨合金焊芯的钴基堆焊焊条  ，采用直流反接  ，渣覆盖性好  ，成形美观  ，具有优良的耐磨、耐热、耐腐蚀性  ，在650℃高温也能保持这些特性 。   用途：用于牙轮钻头轴承、锅炉的旋转叶轮、粉碎机刃口、螺旋送料机等磨损部件的堆焊 。   熔敷金属化学成分/%  C 1.75-3 Si≤2  Mn≤2 Cr 25-33 Fe≤5 W 11-19 其他≤4 余量为Co堆焊硬度HRC：≥53  D842钴基堆焊焊条  型号：EDCoCr-D-03  说明：钴基4号低碳钴基铬钨合金焊芯堆焊焊条  ，采用直流反接  ，堆焊金属在800℃仍能保持良好的抗热疲劳性和耐蚀性 。   用途：用于高温条件下承受冲击和冷热交错的工件堆焊  ，如热锻模  ，阀门密封面等  ，具有良好的性能 。   熔敷金属化学成分/%  C 0.5-0.5 Si≤2  Mn≤2 Cr 23-32 Fe≤5 W≤9.5 其他≤7 余量为Co堆焊硬度HRC：28-35   D852钴基堆焊焊条  型号：EDCoCr-E-04   说明：用于耐高温磨损堆焊焊条,工作温度1100℃,具有红硬性,抗烈性.也可用于高温,高压阀门热段模等,同时经受冲击和高温,耐蚀的部件. HRC≥44  D862钴基堆焊焊条 型号：EDCoCr-E-05      说明：适用于高温磨性磨损及细颗粒小角度冲蚀磨损工况 。 单层堆焊即可满足性能要求  ，**工作温度1000℃,堆焊层硬度：20℃--HRC:64-66、工作温度600℃--HRC：48-52、工作温度800℃--HRC：38-42典型应用领域、工况及部分  ，炼铁、炼焦、烧洁、水泥等工作领域存在高温磨损的机械设备 。   用途：用于堆焊高温工件下服役的烧洁单辊破碎机齿冠篦板及高炉旋转布料溜槽  ，耐磨效果显著